Celstran? POM-GF25-04 AF3001

Acetal (POM) Copolymer

Celanese Corporation

25% 長玻璃纖維

產品說明：

Material code according to ISO 1043-1: POM

Acetal copolymer reinforced with 25 weight percent long glass fibers. The fibers are chemically coupled to the POM matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.

Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.

The very isotropic shrinkage in the molded parts minimizes the warpage.

Complex parts can be manufactured with high reproducibility by injection molding.

Application field: Functionial/structural parts for automotive

物性信息：

基本信息

填料/增強材料	長玻璃纖維, 25% 填料按重量
特性	剛性，高 高強度 共聚物 化學耦合 抗撞擊性，良好 良好的抗蠕變性 耐低溫沖擊
用途	汽車領域的應用
RoHS 合規性	聯系制造商
形式	粒子
加工方法	注射成型
樹脂ID (ISO 1043)	POM

物理性能額定值單位制測試方法

密度	1.59	g/cm3	ISO 1183

機械性能額定值單位制測試方法

拉伸模量	10300	MPa	ISO 527-2/1A/1
拉伸應力 (斷裂)	177	MPa	ISO 527-2/1A/5
拉伸應變 (斷裂)	2.4	%	ISO 527-2/1A/5
彎曲模量 (23°C)	9190	MPa	ISO 178
彎曲應力 (23°C)	265	MPa	ISO 178

沖擊性能額定值單位制測試方法

簡支梁缺口沖擊強度 (23°C)	35	kJ/m2	ISO 179/1eA

注射額定值單位制

干燥溫度	80.0 到 90.0	°C
干燥時間	3.0	hr
建議的最大水分含量	0.15	%
料筒后部溫度	180 到 195	°C
料筒中部溫度	190 到 200	°C
料筒前部溫度	195 到 205	°C
射嘴溫度	195 到 205	°C
加工（熔體）溫度	195 到 205	°C
模具溫度	70.0 到 110	°C
注塑壓力	60.0 到 120	MPa
注射速度	中等
保壓	60.0 到 120	MPa
背壓	0.00 到 3.00	MPa